Aluminum

EN AW 5454 | Al Mg3Mn

On this page you can find the chemical and mechanical specifications of the alloy EN AW 5454 | Al Mg3Mn.

Other dimensions and alloys are available on request.

Our aluminum specialists in Wörth are happy to advise you. We look forward to hearing from you.

Heat-treated condition 0/H111 | EN AW 5454

Mechanical properties

Nominal thickness
mm
Brinell hardness
HBW
Yield strength
Rp0,2 MPa
min./max.
Tensile strength
Rm MPa
min./max.
Elongation
A50
mm %
min.
Elongation
A %
min.
Bending radius
180° t
min.
Bending radius
90° t
min.
0,2 - 0,55885215 - 275120,5 t0,5 t
0,5 - 1,55885215 - 275130,5 t0,5 t
1,5 - 35885215 - 275151,0 t1,0 t
3 - 65885215 - 275171,5 t
6 - 12,55885215 - 275182,5 t
12,5 - 805885215 - 27516

Chemical composition [% max. or range]

SiFeCuMnMgCrNiZnTiGaV
0,250,40,10,50–1,02,4–3,00,05–0,200,250,2

Heat-treated condition H14 | EN AW 5454

Mechanical properties

Nominal thickness
mm
Brinell hardness
HBW
Yield strength
Rp0,2 MPa
min./max.
Tensile strength
Rm MPa
min./max.
Elongation
A50
mm %
min.
Elongation
A %
min.
Bending radius
180° t
min.
Bending radius
90° t
min.
0,2 - 0,581220270 - 3252
0,5 - 1,581220270 - 3253
1,5 - 381220270 - 3253
3 - 681220270 - 3254
6 - 12,581220270 - 3255
12,5 - 2581220270 - 3254

Heat-treated condition H22 | EN AW 5454

Mechanical properties

Nominal thickness
mm
Brinell hardness
HBW
Yield strength
Rp0,2 MPa
min./max.
Tensile strength
Rm MPa
min./max.
Elongation
A50
mm %
min.
Elongation
A %
min.
Bending radius
180° t
min.
Bending radius
90° t
min.
0,2 - 0,574180250 - 30551,5 t0,5 t
0,5 - 1,574180250 - 30561,5 t1,0 t
1,5 - 374180250 - 30572,0 t2,0 t
3 - 674180250 - 30582,5 t
6 - 12,574180250 - 305104,0 t
12,5 - 4074180250 - 3059

Heat-treated condition H24 | EN AW 5454

Mechanical properties

Nominal thickness
mm
Brinell hardness
HBW
Yield strength
Rp0,2 MPa
min./max.
Tensile strength
Rm MPa
min./max.
Elongation
A50
mm %
min.
Elongation
A %
min.
Bending radius
180° t
min.
Bending radius
90° t
min.
0,2 - 0,580200270 - 32542,5 t1,0 t
0,5 - 1,580200270 - 32552,5 t2,0 t
1,5 - 380200270 - 32563,0 t2,5 t
3 - 680200270 - 32573,0 t
6 - 12,580200270 - 32584,0 t
12,5 - 2580200270 - 3257

Heat-treated condition H26 | EN AW 5454

Mechanical properties

Nominal thickness
mm
Brinell hardness
HBW
Yield strength
Rp0,2 MPa
min./max.
Tensile strength
Rm MPa
min./max.
Elongation
A50
mm %
min.
Elongation
A %
min.
Bending radius
180° t
min.
Bending radius
90° t
min.
0,2 - 0,587230290 - 3453
0,5 - 1,587230290 - 3453
1,5 - 387230290 - 3454
3 - 687230290 - 3455

Heat-treated condition H28 | EN AW 5454

Mechanical properties

Nominal thickness
mm
Brinell hardness
HBW
Yield strength
Rp0,2 MPa
min./max.
Tensile strength
Rm MPa
min./max.
Elongation
A50
mm %
min.
Elongation
A %
min.
Bending radius
180° t
min.
Bending radius
90° t
min.
0,2 - 0,5932503103
0,5 - 1,5932503103
1,5 - 3932503103