EN AW 5049 | Al Mg2Mn0.8
On this page you can find the chemical and mechanical specifications of the alloy EN AW 5049 | Al Mg2Mn0.8.
Other dimensions and alloys are available on request.
Our aluminum specialists in Mannheim are happy to advise you. EN AW 5049 - send request!
Chemical composition [% max. or range]
| Si | Fe | Cu | Mn | Mg | Cr | Ni | Zn | Ti | Ga | V |
| 0.4 | 0.5 | 0.1 | 0.50–1.1 | 1.6–2.5 | 0.3 | — | 0.2 | 0.1 | — | — |
EN AW 5049 | Al Mg2Mn0.8: Heat-treated condition 0/H111
Mechanical properties
| Nominal thickness mm | Brinell hardness HBW | Yield strength Rp0,2 MPa min./max. | Tensile strength Rm MPa min./max. | Elongation A50 mm % min. | Elongation A % min. | Bending radius 180° t min. | Bending radius 90° t min. |
| 0.2 - 0.5 | 52 | 80 | 190 - 240 | 12 | 0.5 t | 0 t | |
| 0.5 - 1.5 | 52 | 80 | 190 - 240 | 14 | 0.5 t | 0.5 t | |
| 1.5 - 3 | 52 | 80 | 190 - 240 | 16 | 1.0 t | 1.0 t | |
| 3 - 6 | 52 | 80 | 190 - 240 | 18 | 1.0 t | 1.0 t | |
| 6 - 12.5 | 52 | 80 | 190 - 240 | 18 | 2.0 t | ||
| 12.5 - 100 | 52 | 80 | 190 - 240 | 17 |
EN AW 5049 | Al Mg2Mn0.8: Heat-treated condition H14
Mechanical properties
| Nominal thickness mm | Brinell hardness HBW | Yield strength Rp0,2 MPa min./max. | Tensile strength Rm MPa min./max. | Elongation A50 mm % min. | Elongation A % min. | Bending radius 180° t min. | Bending radius 90° t min. |
| 0.2 - 0.5 | 72 | 190 | 240 - 280 | 3 | |||
| 0.5 - 1.5 | 72 | 190 | 240 - 280 | 3 | |||
| 1.5 - 3 | 72 | 190 | 240 - 280 | 4 | |||
| 3 - 6 | 72 | 190 | 240 - 280 | 4 | |||
| 6 - 12.5 | 72 | 190 | 240 - 280 | 5 | |||
| 12.5 - 25 | 72 | 190 | 240 - 280 | 5 |
EN AW 5049 | Al Mg2Mn0.8: Heat-treated condition H22
Mechanical properties
| Nominal thickness mm | Brinell hardness HBW | Yield strength Rp0,2 MPa min./max. | Tensile strength Rm MPa min./max. | Elongation A50 mm % min. | Elongation A % min. | Bending radius 180° t min. | Bending radius 90° t min. |
| 0.2 - 0.5 | 63 | 130 | 220 - 270 | 7 | 1.5 t | 0.5 t | |
| 0.5 - 1.5 | 63 | 130 | 220 - 270 | 8 | 1.5 t | 1.0 t | |
| 1.5 - 3 | 63 | 130 | 220 - 270 | 10 | 2.0 t | 1.5 t | |
| 3 - 6 | 63 | 130 | 220 - 270 | 11 | 1.5 t | ||
| 6 - 12.5 | 63 | 130 | 220 - 270 | 10 | 2.5 t | ||
| 12.5 - 40 | 63 | 130 | 220 - 270 | 9 |
EN AW 5049 | Al Mg2Mn0.8: Heat-treated condition H24
Mechanical properties
| Nominal thickness mm | Brinell hardness HBW | Yield strength Rp0,2 MPa min./max. | Tensile strength Rm MPa min./max. | Elongation A50 mm % min. | Elongation A % min. | Bending radius 180° t min. | Bending radius 90° t min. |
| 0.2 - 0.5 | 70 | 160 | 240 - 280 | 6 | 2.5 t | 1.0 t | |
| 0.5 - 1.5 | 70 | 160 | 240 - 280 | 6 | 2.5 t | 1.5 t | |
| 1.5 - 3 | 70 | 160 | 240 - 280 | 7 | 2.5 t | 2.0 t | |
| 3 - 6 | 70 | 160 | 240 - 280 | 8 | 2.5 t | ||
| 6 - 12.5 | 70 | 160 | 240 - 280 | 10 | 3.0 t | ||
| 12.5 - 25 | 70 | 160 | 240 - 280 | 8 |
EN AW 5049 | Al Mg2Mn0.8: Heat-treated condition H26
Mechanical properties
| Nominal thickness mm | Brinell hardness HBW | Yield strength Rp0,2 MPa min./max. | Tensile strength Rm MPa min./max. | Elongation A50 mm % min. | Elongation A % min. | Bending radius 180° t min. | Bending radius 90° t min. |
| 0.2 - 0.5 | 78 | 190 | 265 - 305 | 4 | 1.5 t | ||
| 0.5 - 1.5 | 78 | 190 | 265 - 305 | 4 | 2.0 t | ||
| 1.5 - 3 | 78 | 190 | 265 - 305 | 5 | 3.0 t | ||
| 3 - 6 | 78 | 190 | 265 - 305 | 6 | 3.5 t |
EN AW 5049 | Al Mg2Mn0.8: Heat-treated condition H28
Mechanical properties
| Nominal thickness mm | Brinell hardness HBW | Yield strength Rp0,2 MPa min./max. | Tensile strength Rm MPa min./max. | Elongation A50 mm % min. | Elongation A % min. | Bending radius 180° t min. | Bending radius 90° t min. |
| 0.2 - 0.5 | 87 | 230 | 290 | 3 | |||
| 0.5 - 1.5 | 87 | 230 | 290 | 3 | |||
| 1.5 - 3 | 87 | 230 | 290 | 4 |