EN AW 5052 | Al Mg2.5
On this page you can find the chemical and mechanical specifications of the alloy EN AW 5052 | Al Mg2.5.
Other dimensions and alloys are available on request.
Our aluminum specialists in Mannheim are happy to advise you. EN AW 5052 - send request!
Chemical composition [% max. or range]
Si | Fe | Cu | Mn | Mg | Cr | Ni | Zn | Ti | Ga | V |
0.4 | 0.5 | 0.1 | 0.50–1.1 | 1.6–2.5 | 0.3 | — | 0.2 | 0.1 | — | — |
EN AW 5052 | Al Mg2.5: Heat-treated condition 0/H111
Mechanical properties
Nominal thickness mm | Brinell hardness HBW | Yield strength Rp0,2 MPa min./max. | Tensile strength Rm MPa min./max. | Elongation A50 mm % min. | Elongation A % min. | Bending radius 180° t min. | Bending radius 90° t min. |
0.2 - 0.5 | 47 | 65 | 170 - 215 | 12 | 0 t | 0 t | |
0.5 - 1.5 | 47 | 65 | 170 - 215 | 14 | 0 t | 0 t | |
1.5 - 3 | 47 | 65 | 170 - 215 | 16 | 0.5 t | 0.5 t | |
3 - 6 | 47 | 65 | 170 - 215 | 18 | 1.0 t | ||
6 - 12.5 | 46 | 65 | 165 - 215 | 19 | 2.0 t | ||
12.5 - 80 | 46 | 65 | 165 - 215 | 18 |
EN AW 5052 | Al Mg2.5: Heat-treated condition H14
Mechanical properties
Nominal thickness mm | Brinell hardness HBW | Yield strength Rp0,2 MPa min./max. | Tensile strength Rm MPa min./max. | Elongation A50 mm % min. | Elongation A % min. | Bending radius 180° t min. | Bending radius 90° t min. |
0.2 - 0.5 | 69 | 180 | 230 - 280 | 3 | |||
0.5 - 1.5 | 69 | 180 | 230 - 280 | 3 | |||
1.5 - 3 | 69 | 180 | 230 - 280 | 4 | |||
3 - 6 | 69 | 180 | 230 - 280 | 4 | |||
6 - 12.5 | 69 | 180 | 230 - 280 | 5 | |||
12.5 - 25 | 69 | 180 | 230 - 280 | 4 |
EN AW 5052 | Al Mg2.5: Heat-treated condition H22
Mechanical properties
Nominal thickness mm | Brinell hardness HBW | Yield strength Rp0,2 MPa min./max. | Tensile strength Rm MPa min./max. | Elongation A50 mm % min. | Elongation A % min. | Bending radius 180° t min. | Bending radius 90° t min. |
0.2 - 0.5 | 61 | 130 | 210 - 260 | 5 | 1.5 t | 0.5 t | |
0.5 - 1.5 | 61 | 130 | 210 - 260 | 6 | 1.5 t | 1.0 t | |
1.5 - 3 | 61 | 130 | 210 - 260 | 7 | 1.5 t | 1.5 t | |
3 - 6 | 61 | 130 | 210 - 260 | 10 | 1.5 t | ||
6 - 12.5 | 61 | 130 | 210 - 260 | 12 | 2.5 t | ||
12.5 - 40 | 61 | 130 | 210 - 260 | 12 |
EN AW 5052 | Al Mg2.5: Heat-treated condition H24
Mechanical properties
Nominal thickness mm | Brinell hardness HBW | Yield strength Rp0,2 MPa min./max. | Tensile strength Rm MPa min./max. | Elongation A50 mm % min. | Elongation A % min. | Bending radius 180° t min. | Bending radius 90° t min. |
0.2 - 0.5 | 67 | 150 | 230 - 280 | 4 | 2.0 t | 0.5 t | |
0.5 - 1.5 | 67 | 150 | 230 - 280 | 5 | 2.0 t | 1.5 t | |
1.5 - 3 | 67 | 150 | 230 - 280 | 6 | 2.0 t | 2.0 t | |
3 - 6 | 67 | 150 | 230 - 280 | 7 | 2.5 t | ||
6 - 12.5 | 67 | 150 | 230 - 280 | 9 | 3.0 t | ||
12.5 - 25 | 67 | 150 | 230 - 280 | 9 |
EN AW 5052 | Al Mg2.5: Heat-treated condition H26
Mechanical properties
Nominal thickness mm | Brinell hardness HBW | Yield strength Rp0,2 MPa min./max. | Tensile strength Rm MPa min./max. | Elongation A50 mm % min. | Elongation A % min. | Bending radius 180° t min. | Bending radius 90° t min. |
0.2 - 0.5 | 74 | 180 | 250 - 300 | 3 | 1.5 t | ||
0.5 - 1.5 | 74 | 180 | 250 - 300 | 4 | 2.0 t | ||
1.5 - 3 | 74 | 180 | 250 - 300 | 5 | 3.0 t | ||
3 - 6 | 74 | 180 | 250 - 300 | 6 | 3.5 t |
EN AW 5052 | Al Mg2.5: Heat-treated condition H28
Mechanical properties
Nominal thickness mm | Brinell hardness HBW | Yield strength Rp0,2 MPa min./max. | Tensile strength Rm MPa min./max. | Elongation A50 mm % min. | Elongation A % min. | Bending radius 180° t min. | Bending radius 90° t min. |
0.2 - 0.5 | 81 | 210 | 270 | 3 | |||
0.5 - 1.5 | 81 | 210 | 270 | 3 | |||
1.5 - 3 | 81 | 210 | 270 | 4 |