On this page you can find the chemical and mechanical specifications of the alloy EN AW 5454 | Al Mg3Mn.
Other dimensions and alloys are available on request.
Our aluminum specialists in Mannheim are happy to advise you. EN AW 5454 - send request!
EN AW 5454 | Al Mg3Mn: Heat-treated condition 0/H111
Mechanical properties
| Nominal thickness mm | Brinell hardness HBW | Yield strength Rp0,2 MPa min./max. | Tensile strength Rm MPa min./max. | Elongation A50 mm % min. | Elongation A % min. | Bending radius 180° t min. | Bending radius 90° t min. |
| 0.2 - 0.5 | 58 | 85 | 215 - 275 | 12 | 0.5 t | 0.5 t | |
| 0.5 - 1.5 | 58 | 85 | 215 - 275 | 13 | 0.5 t | 0.5 t | |
| 1.5 - 3 | 58 | 85 | 215 - 275 | 15 | 1.0 t | 1.0 t | |
| 3 - 6 | 58 | 85 | 215 - 275 | 17 | 1.5 t | ||
| 6 - 12.5 | 58 | 85 | 215 - 275 | 18 | 2.5 t | ||
| 12.5 - 80 | 58 | 85 | 215 - 275 | 16 |
EN AW 5454 | Al Mg3Mn: Chemical composition [% max. or range]
| Si | Fe | Cu | Mn | Mg | Cr | Ni | Zn | Ti | Ga | V |
| 0.25 | 0.4 | 0.1 | 0.50–1.0 | 2.4–3.0 | 0.05–0.20 | — | 0.25 | 0.2 | — | — |
EN AW 5454 | Al Mg3Mn: Heat-treated condition H14
Mechanical properties
| Nominal thickness mm | Brinell hardness HBW | Yield strength Rp0,2 MPa min./max. | Tensile strength Rm MPa min./max. | Elongation A50 mm % min. | Elongation A % min. | Bending radius 180° t min. | Bending radius 90° t min. |
| 0.2 - 0.5 | 81 | 220 | 270 - 325 | 2 | |||
| 0.5 - 1.5 | 81 | 220 | 270 - 325 | 3 | |||
| 1.5 - 3 | 81 | 220 | 270 - 325 | 3 | |||
| 3 - 6 | 81 | 220 | 270 - 325 | 4 | |||
| 6 - 12.5 | 81 | 220 | 270 - 325 | 5 | |||
| 12.5 - 25 | 81 | 220 | 270 - 325 | 4 |
EN AW 5454 | Al Mg3Mn: Heat-treated condition H22
Mechanical properties
| Nominal thickness mm | Brinell hardness HBW | Yield strength Rp0,2 MPa min./max. | Tensile strength Rm MPa min./max. | Elongation A50 mm % min. | Elongation A % min. | Bending radius 180° t min. | Bending radius 90° t min. |
| 0.2 - 0.5 | 74 | 180 | 250 - 305 | 5 | 1.5 t | 0.5 t | |
| 0.5 - 1.5 | 74 | 180 | 250 - 305 | 6 | 1.5 t | 1.0 t | |
| 1.5 - 3 | 74 | 180 | 250 - 305 | 7 | 2.0 t | 2.0 t | |
| 3 - 6 | 74 | 180 | 250 - 305 | 8 | 2.5 t | ||
| 6 - 12.5 | 74 | 180 | 250 - 305 | 10 | 4.0 t | ||
| 12.5 - 40 | 74 | 180 | 250 - 305 | 9 |
EN AW 5454 | Al Mg3Mn: Heat-treated condition H24
Mechanical properties
| Nominal thickness mm | Brinell hardness HBW | Yield strength Rp0,2 MPa min./max. | Tensile strength Rm MPa min./max. | Elongation A50 mm % min. | Elongation A % min. | Bending radius 180° t min. | Bending radius 90° t min. |
| 0.2 - 0.5 | 80 | 200 | 270 - 325 | 4 | 2.5 t | 1.0 t | |
| 0.5 - 1.5 | 80 | 200 | 270 - 325 | 5 | 2.5 t | 2.0 t | |
| 1.5 - 3 | 80 | 200 | 270 - 325 | 6 | 3.0 t | 2.5 t | |
| 3 - 6 | 80 | 200 | 270 - 325 | 7 | 3.0 t | ||
| 6 - 12.5 | 80 | 200 | 270 - 325 | 8 | 4.0 t | ||
| 12.5 - 25 | 80 | 200 | 270 - 325 | 7 |
EN AW 5454 | Al Mg3Mn: Heat-treated condition H26
Mechanical properties
| Nominal thickness mm | Brinell hardness HBW | Yield strength Rp0,2 MPa min./max. | Tensile strength Rm MPa min./max. | Elongation A50 mm % min. | Elongation A % min. | Bending radius 180° t min. | Bending radius 90° t min. |
| 0.2 - 0.5 | 87 | 230 | 290 - 345 | 3 | |||
| 0.5 - 1.5 | 87 | 230 | 290 - 345 | 3 | |||
| 1.5 - 3 | 87 | 230 | 290 - 345 | 4 | |||
| 3 - 6 | 87 | 230 | 290 - 345 | 5 |
EN AW 5454 | Al Mg3Mn: Heat-treated condition H28
Mechanical properties
| Nominal thickness mm | Brinell hardness HBW | Yield strength Rp0,2 MPa min./max. | Tensile strength Rm MPa min./max. | Elongation A50 mm % min. | Elongation A % min. | Bending radius 180° t min. | Bending radius 90° t min. |
| 0.2 - 0.5 | 93 | 250 | 310 | 3 | |||
| 0.5 - 1.5 | 93 | 250 | 310 | 3 | |||
| 1.5 - 3 | 93 | 250 | 310 | 3 |