High-strength IF steel | HX180YD - HX300YD

Choose your high-strength IF steel here in grades HX180YD, HX220YD, HX260YD and HX300YD.

The experts at our locations are happy to advise you. We look forward to hearing from you.

Properties of high-strength IF steel HX180YD - HX300YD | DIN EN 10 346

Steel type

Short designation	VDA239-100*	Surface finish	Material number
HX180YD	CR180IF	+Z,+ZF,+ZA,+ZM,+AZ,+AS	1.0921
HX220YD	CR210IF	+Z,+ZF,+ZA,+ZM,+AZ,+AS	1.0923
HX260YD	CR240IF	+Z,+ZF,+ZA,+ZM,+AZ,+AS	1.0926
HX300YD	-	+Z,+ZF,+ZA,+ZM,+AZ,+AS	1.0927

* Comparative grade, therefore minor deviations from DIN EN values possible

Mechanical properties (transverse)

Short designation	Proof stress R_p0.2¹⁾ MPa	Tensile strength R_m MPa	Elongation at fracture A₈₀²⁾³⁾ %	Anisotropy r₉₀ ³⁾⁴⁾⁵⁾ min.	Strain hardening exponent n₉₀⁵⁾min.	Bake hardening index BH₂ min.
HX180YD	180-240	330-390	34	1.7	0.18	-
HX220YD	220-280	340-420	32	1.5	0.17	-
HX260YD	260-320	380-440	30	1.4	0.16	-
HX300YD	300-360	390-470	27	1.3	0.15	-

Chemical composition (heat analysis)

Short designation	Percentage by weight % max.
	C	Si	Mn	P	S	AI min.	Nb	Ti
HX180YD	0.01	0.30	0.70	0.060	0.025	0.010	0.09	0.12
HX220YD	0.01	0.30	0.90	0.080	0.025	0.010	0.09	0.12
HX260YD	0.01	0.30	1.60	0.10	0.025	0.010	0.09	0.12
HX300YD	0.015	0.30	1.60	0.10	0.025	0.010	0.09	0.12

Your product of choice: HX180YD - HX300YD

Send request!

1) Where the yield strength is defined, the respective values shall apply to the lower yield strength (R_eL).

2) Depending on the product thickness, the minimum values of elongation at fracture are reduced as follows: 0.50 mm < t < 0.70 mm (minus 2 units), 0.35 mm < t < 0.50 mm (minus 4 units), and t < 0,35 mm (minus 7 units).

3) For AS, AZ, ZF and ZM coatings, the minimum A₈₀ value is reduced by 2 units and the minimum r₉₀ value by 0.2.

4) For product thicknesses of 1.5 mm < t < 2 mm, the minimum r₉₀ value is reduced by 0.2, and for t ≥ 2 mm by 0.4.

5) Depending on the product thickness, the minimum r₉₀ value is reduced as follows: 0.50 mm < t < 0.70 mm by 0.2; 0.35 mm < t < 0.50 mm by 0.4, and t < 0.35 mm by 0.6. Also depending on the product thickness, the minimum n90 value is reduced as follows: 0.50 mm < t < 0.70 mm by 0.01; 0.35 mm < t < 0.50 mm by 0.03, and t < 0.35 mm by 0.04.

*Comparative grade, therefore minor deviations from DIN EN values possible