Retained-austenite steel (TRIP-steel)
HCT690T - HCT780T

Choose your hot-dip coated retained-austenite steel (TRIP steel) in grades HCT690T and HCT780T here.

The experts at our locations are happy to advise you. We look forward to hearing from you.

Properties according to DIN EN 10 346

Steel type, cold rolled

Short designation	VDA239-100*	Surface finish	Material number
HCT690T	CR400Y690T-TR	+Z	1.0947
HCT780T	CR450Y780T-TR	+Z	1.0948

Mechanical properties, longitudinal

Short designation	Proof stress R_p0,2 MPa	Tensile strength R_m MPa min.	Elongation at fracture A₈₀¹⁾²⁾ % min.	Strain hardening exponent n_10-UE min.	Bake hardening index BH₂ min.
HCT690T	400-520	690	23	0.19	40
HCT780T	450-570	780	21	0.16	40

Chemical composition, heat analysis

Percentage by weight % max.
Short designation	C	Si	Mn	P	S	Al_total(span)	Cr+Mo	Nb+Ti	V	B
HCT690T	0.24	2.00	2.20	0.080	0.015	0.015-2.0	0.60	0.20	0.20	0.005
HCT780T	0.25	2.20	2.50	0.080	0.015	0.015-2.0	0.60	0.20	0.20	0.005

Your product of choice: Retained-austenite steel (TRIP-steel) | HCT690T - HCT780T

Send request

1) Reduced minimum values of elongation at rupture apply to product thicknesses t < 0.60 mm (minus 2 units).
2) For ZF-coated, products the minimum values of elongation at fracture are reduced by 2 unites.
For ZF-coated in thicknesses t < 0.60 mm, the minimum elongation at rupture is reduced by 4 units.

* Comparative grade, therefore minor deviations from DIN EN values possible

Retained-austenite steel (TRIP-steel) HCT690T - HCT780T