Complex-phase steel | HDT760C
Choose your complex-phase steel here in the grades HDT760C.
The experts at our locations are happy to advise you. Complex-phase steel - we look forward to hearing from you.
Properties according to DIN EN 10 338
Steel type
| Short designation | VDA239-100* | Material number |
| HDT760C | HR660Y760T-CP | 1.0998 |
* Comparative grade, therefore minor deviations from DIN EN values possible
Complex-phase steel: Mechanical properties, longitudinal
| Short designation | Proof stress Rp0.2 MPa | Tensile strength Rm MPA min. | Elongation at fracture A80 % min. | Elongation at fracture A1) % min. |
| HDT760C | 660-830 | 760 | 10 | 12 |
Complex-phase steel: Chemical composition, heat analysis
| Percentage by weight % max. | ||||||||||
| Short designation | C | Si | Mn | P | S | AItotal (span) | Cr+Mo | Nb+Ti | V | B |
| HDT760C | 0.18 | 1.00 | 2.50 | 0.080 | 0.015 | 0.015-2.0 | 1.00 | 0.25 | 0.20 | 0.005 |
Your product of choice: HDT760C
1) Percentage elongation after fracture using a proportional specimen with L0 = 5.65 √S0 for sheet thicknesses ≥ 3.0 mm