S235J2 | 1.0117

Grade S235J2 has a minimum yield strength of 235 MPa. The impact energy at a test temperature of -20°C is at least 27 joules.

Non-alloy/general structural steel

Short designation	VDA239-100*	Material number
S235J2	-	1.0117

* Comparative grade, therefore minor deviations from DIN EN values possible

Upper yield strength ReH MPa min.	Tensile strength Rm MPa		Elongation at fracture A80 % min.					Elongation at fracture A 5 % min.
e ≤ 16 mm	e < 3 mm	3 mm ≤ e ≤ 16 mm	e ≤ 1 mm	1 mm < e ≤ 1.5 mm	1.5 mm < e ≤ 2 mm	2 mm < e ≤ 2.5 mm	2.5 mm < e < 3 mm	3 mm ≤ e ≤ 16 mm
235	360-510	360–510	15	16	17	18	19	24

1) As rolling widths ≥ 600 mm are primarily used, transverse values generally apply, refer to DIN EN 10 025-2.