EN AW 6082A | Al Si1MgMn(A)
On this page you can find the chemical and mechanical specifications of the alloy EN AW 6082A | Al Si1MgMn(A).
Other dimensions and alloys are available on request.
Our aluminum specialists in Wörth are happy to advise you. EN AW 6082A - send request!
EN AW 6082A | Al Si1MgMn(A): Chemical composition [% max. oder range]
| Si | Fe | Cu | Mn | Mg | Cr | Ni | Zn | Ti | Ga | V |
| 0.7–1.3 | 0.5 | 0.1 | 0.40–1.0 | 0.6–1.2 | 0.3 | — | 0.2 | 0.1 | — | — |
EN AW 6082A | Al Si1MgMn(A): Heat-treated condition T4
Mechanical properties
| Nominal thickness mm | Brinell hardness HBW | Yield strength Rp0,2 MPa min./max. | tensile strength Rm MPa min./max. | Elongation A50 mm % min. | Elongation A % min. | Bending radius 180° t min. | Bending radius 90° t min. |
| >= 0.4 - 1.5 | 58 | 110 | 205 | 12 | 3.0 t | 1.5 t | |
| 1.5 - 3 | 58 | 110 | 205 | 14 | 3.0 t | 2.0 t | |
| 3 - 6 | 58 | 110 | 205 | 15 | 3.0 t | ||
| 6 - 12.5 | 58 | 110 | 205 | 14 | 4.0 t | ||
| 12.5 - 40 | 58 | 110 | 205 | 13 | |||
| 40 - 80 | 58 | 110 | 205 | 12 |
EN AW 6082A | Al Si1MgMn(A): Heat-treated condition T6
Mechanical properties
| Nominal thickness mm | Brinell hardness HBW | Yield strength Rp0,2 MPa min./max. | Tensile strength Rm MPa min./max. | Elongation A50 mm % min. | Elongation A % min. | Bending radius 180° t min. | Bending radius 90° t min. |
| >= 0.4 - 1.5 | 94 | 260 | 310 | 6 | 2.5 t | ||
| 1.5 - 3 | 94 | 260 | 310 | 7 | 3.5 t | ||
| 3 - 6 | 94 | 260 | 310 | 10 | 4.5 t | ||
| 6 - 12.5 | 91 | 255 | 300 | 9 | 6.0 t | ||
| 12.5 - 60 | 89 | 240 | 295 | 8 | |||
| 60 - 100 | 89 | 240 | 295 | 7 | |||
| 100 - 150 | 84 | 240 | 275 | 6 | |||
| 150 - 175 | 83 | 230 | 275 | 4 | |||
| 175 - 350 | 220 | 260 | 2 |