EN AW 5083 | Al Mg4,5Mn0,7
On this page you can find the chemical and mechanical specifications of the alloy EN AW 5083 | Al Mg4,5Mn0,7.
Other dimensions and alloys are available on request.
Our aluminum specialists in Wörth are happy to advise you. EN AW 5083 - send request!
EN AW 5083 | Al Mg4,5Mn0,7: Heat-treated condition 0/H111
Mechanical properties
| Nominal thickness mm | Brinell hardness HBW | Yield strength Rp0,2 MPa min./max. | Tensile strength Rm MPa min./max. | Elongation A50 mm % min. | Elongation A % min. | Bending radius 180° t min. | Bending radius 90° t min. |
| 0,2 - 0,5 | 75 | 125 | 275 - 350 | 11 | 1,0 t | 0,5 t | |
| 0,5 - 1,5 | 75 | 125 | 275 - 350 | 12 | 1,0 t | 1,0 t | |
| 1,5 - 3 | 75 | 125 | 275 - 350 | 13 | 1,5 t | 1,0 t | |
| 3 - 6 | 75 | 125 | 275 - 350 | 15 | 1,5 t | ||
| 6 - 12,5 | 75 | 115 | 270 - 345 | 16 | 2,5 t | ||
| 12,5 - 50 | 75 | 115 | 270 - 345 | 15 | |||
| 50 - 80 | 73 | 115 | 270 - 345 | 14 | |||
| 80 - 120 | 70 | 110 | 260 | 12 | |||
| 120 - 200 | 69 | 105 | 255 | 12 | |||
| 200 - 250 | 69 | 95 | 250 | 10 | |||
| 250 - 300 | 69 | 90 | 245 | 9 |
EN AW 5083 | Al Mg4,5Mn0,7: Chemical composition [% max. or range]
| Si | Fe | Cu | Mn | Mg | Cr | Ni | Zn | Ti | Ga | V |
| 0,4 | 0,4 | 0,1 | 0,40–1,0 | 4,0–4,9 | 0,05–0,25 | — | 0,25 | 0,15 | — | — |
EN AW 5083 | Al Mg4,5Mn0,7: Heat-treated condition H14
Mechanical properties
| Nominal thickness mm | Brinell hardness HBW | Yield strength Rp0,2 MPa min./max. | Tensile strength Rm MPa min./max. | Elongation A50 mm % min. | Elongation A % min. | Bending radius 180° t min. | Bending radius 90° t min. |
| 0,2 - 0,5 | 102 | 280 | 340 - 400 | 2 | |||
| 0,5 - 1,5 | 102 | 280 | 340 - 400 | 3 | |||
| 1,5 - 3 | 102 | 280 | 340 - 400 | 3 | |||
| 3 - 6 | 102 | 280 | 340 - 400 | 3 | |||
| 6 - 12,5 | 102 | 280 | 340 - 400 | 4 | |||
| 12,5 - 25 | 102 | 280 | 340 - 400 | 3 |
EN AW 5083 | Al Mg4,5Mn0,7: Heat-treated condition H22
Mechanical properties
| Nominal thickness mm | Brinell hardness HBW | Yield strength Rp0,2 MPa min./max. | Tensile strength Rm MPa min./max. | Elongation A50 mm % min. | Elongation A % min. | Bending radius 180° t min. | Bending radius 90° t min. |
| 0,2 - 0,5 | 89 | 215 | 305 - 380 | 5 | 2,0 t | 0,5 t | |
| 0,5 - 1,5 | 89 | 215 | 305 - 380 | 6 | 2,0 t | 1,5 t | |
| 1,5 - 3 | 89 | 215 | 305 - 380 | 7 | 3,0 t | 2,0 t | |
| 3 - 6 | 89 | 215 | 305 - 380 | 8 | 2,5 t | ||
| 6 - 12,5 | 89 | 215 | 305 - 380 | 10 | 3,5 t | ||
| 12,5 - 40 | 89 | 215 | 305 - 380 | 9 |
EN AW 5083 | Al Mg4,5Mn0,7: Heat-treated condition H24
Mechanical properties
| Nominal thickness mm | Brinell hardness HBW | Yield strength Rp0,2 MPa min./max. | Tensile strength Rm MPa min./max. | Elongation A50 mm % min. | Elongation A % min. | Bending radius 180° t min. | Bending radius 90° t min. |
| 0,2 - 0,5 | 99 | 250 | 340 - 400 | 4 | 1,0 t | ||
| 0,5 - 1,5 | 99 | 250 | 340 - 400 | 5 | 2,0 t | ||
| 1,5 - 3 | 99 | 250 | 340 - 400 | 6 | 2,5 t | ||
| 3 - 6 | 99 | 250 | 340 - 400 | 7 | 3,5 t | ||
| 6 - 12,5 | 99 | 250 | 340 - 400 | 8 | 4,5 t | ||
| 12,5 - 25 | 99 | 250 | 340 - 400 | 7 |
EN AW 5083 | Al Mg4,5Mn0,7: Heat-treated condition H26
Mechanical properties
| Nominal thickness mm | Brinell hardness HBW | Yield strength Rp0,2 MPa min./max. | Tensile strength Rm MPa min./max. | Elongation A50 mm % min. | Elongation A % min. | Bending radius 180° t min. | Bending radius 90° t min. |
| 0,2 - 0,5 | 106 | 280 | 360 - 420 | 2 | |||
| 0,5 - 1,5 | 106 | 280 | 360 - 420 | 3 | |||
| 1,5 - 3 | 106 | 280 | 360 - 420 | 3 | |||
| 3 - 4 | 106 | 280 | 360 - 420 | 3 |