Aluminum

EN AW 5251 | Al Mg2Mn0,3

On this page you can find the chemical and mechanical specifications of the alloy EN AW 5251 | Al Mg2Mn0,3.

Other dimensions and alloys are available on request.

Our aluminum specialists in Wörth are happy to advise you. We look forward to hearing from you.

Chemical composition [% max. or range]

SiFeCuMnMgCrNiZnTiGaV
0,40,50,150,10–0,501,7–2,40,20,150,15

Heat-treated condition 0/H111 | EN AW 5251

Mechanical properties

Nominal thickness
mm
Brinell hardness
HBW
Yield strength
Rp0,2 MPa
min./max.
Tensile strength
Rm MPa
min./max.
Elongation
A50
mm %
min.
Elongation
A %
min.
Bending radius
180° t
min.
Bending radius
90° t
min.
0,2 - 0,54460160 - 200130 t0 t
0,5 - 1,54460160 - 200140 t0 t
1,5 - 34460160 - 200160,5 t0,5 t
3 - 64460160 - 200181,0 t
6 - 12,54460160 - 200182,0 t
12,5 - 504460160 - 20018

Heat-treated condition H14 | EN AW 5251

Mechanical properties

Nominal thickness
mm
Brinell hardness
HBW
Yield strength
Rp0,2 MPa
min./max.
Tensile strength
Rm MPa
min./max.
Elongation
A50
mm %
min.
Elongation
A %
min.
Bending radius
180° t
min.
Bending radius
90° t
min.
0,2 - 0,564170210 - 25022,5 t0,5 t
0,5 - 1,564170210 - 25022,5 t1,5 t
1,5 - 364170210 - 25032,5 t1,5 t
3 - 664170210 - 25042,5 t
6 - 12,564170210 - 25053,0 t

Heat-treated condition H22 | EN AW 5251

Mechanical properties

Nominal thickness
mm
Brinell hardness
HBW
Yield strength
Rp0,2 MPa
min./max.
Tensile strength
Rm MPa
min./max.
Elongation
A50
mm %
min.
Elongation
A %
min.
Bending radius
180° t
min.
Bending radius
90° t
min.
0,2 - 0,556120190 - 23041,5 t0 t
0,5 - 1,556120190 - 23061,5 t1,0 t
1,5 - 356120190 - 23081,5 t1,0 t
3 - 656120190 - 230101,5 t
6 - 12,556120190 - 230122,5 t
12,5 - 2556120190 - 23012

Heat-treated condition H24 | EN AW 5251

Mechanical properties

Nominal thickness
mm
Brinell hardness
HBW
Yield strength
Rp0,2 MPa
min./max.
Tensile strength
Rm MPa
min./max.
Elongation
A50
mm %
min.
Elongation
A %
min.
Bending radius
180° t
min.
Bending radius
90° t
min.
0,2 - 0,562140210 - 25032,0 t0,5 t
0,5 - 1,562140210 - 25052,0 t1,5 t
1,5 - 362140210 - 25062,0 t1,5 t
3 - 662140210 - 25082,5 t
6 - 12,562140210 - 250103,0 t

Heat-treated condition H26 | EN AW 5251

Mechanical properties

Nominal thickness
mm
Brinell hardness
HBW
Yield strength
Rp0,2 MPa
min./max.
Tensile strength
Rm MPa
min./max.
Elongation
A50
mm %
min.
Elongation
A %
min.
Bending radius
180° t
min.
Bending radius
90° t
min.
0,2 - 0,569170230 - 27033,0 t1,0 t
0,5 - 1,569170230 - 27043,0 t1,5 t
1,5 - 369170230 - 27053,0 t2,0 t
3 - 469170230 - 27073,0 t

Heat-treated condition H28 | EN AW 5251

Mechanical properties

Nominal thickness
mm
Brinell hardness
HBW
Yield strength
Rp0,2 MPa
min./max.
Tensile strength
Rm MPa
min./max.
Elongation
A50
mm %
min.
Elongation
A %
min.
Bending radius
180° t
min.
Bending radius
90° t
min.
0,2 - 0,5772002552
0,5 - 1,5772002553
1,5 - 3772002553