DC01+ZE | 1.0330

DC01+ZE is an electrolytically zinc-coated cold-rolled flat steel for cold forming with a yield strength of max. 280 MPa.

DC01+ZE - send request!

Mild low-carbon steel for cold forming

Properties according to DIN EN 10 152

Steel type

Short designation	VDA239-100*	Surface finish	Material number
DC01	CR1	+ZE	1.0330

* Comparative grade, therefore slight deviations from DIN EN values possible

DC01+ZE | 1.0330: Mechanical properties (transverse)

Yield strength R¹⁾ MPa e max.	Tensile strength Rm MPa	Elongation at fracture²⁾ % A80	Anisotropy r90³⁾⁴⁾min.	Strain hardening exponent n90³⁾ min.
280	270–410	28	-	-

DC01+ZE | 1.0330: Chemical composition (heat analysis)

Percentage by weight % max.
C	P	S	Mn	Ti
0.12	0.045	0.0	0.60	-

Your product of choice: DC01+ZE | 1.0330

Send request!

1) Where no yield strength is defined, the respective values shall apply to the 0.2 % proof stress Rp0.2, otherwise for the lower yield strength (ReL). For thicknesses ≤ 0.7 mm, but > 0.5 mm, the maximum yield strength may be 20 MPa higher, and for thicknesses ≤ 0.5 mm 40 MPa.

2) For thicknesses ≤ 0.7 mm but > 0.5 mm, the minimum elongation at fracture may be 2 units lower. For thicknesses ≤ 0.5 mm, the minimum elongation at fracture may be 4 units lower.

3) The r90 and n90 values shown apply to product thicknesses ≥ 0.5 mm only.

4) For thicknesses > 2 mm, the r90 value is reduced by 0.2.