DC04+ZE | 1.0338

DC04+ZE is an electrolytically zinc-coated cold-rolled flat steel for cold forming with a yield strength of max. 220 MPa.

DC04+ZE – send request!

Mild low-carbon steel for cold forming

Properties according to DIN EN 10 152

Steel type

Short designation	VDA239-100*	Surface finish	Material number
DC04	CR3	+ZE	1.0338

* Comparative grade, therefore slight deviations from DIN EN values possible

DC04+ZE | 1.0338: Mechanical properties (transverse)

Yield strength R¹⁾ MPa e max.	Tensile strength Rm MPa	Elongation at fracture²⁾ % A80	Anisotropy r90³⁾⁴⁾min.	Strain hardening exponent n90³⁾ min.
220	270–350	37	1.6	0.170

DC04+ZE | 1.0338: Chemical composition (heat analysis)

Percentage by weight % max.
C	P	S	Mn	Ti
0.08	0.030	0.0	0.40	-

Your product of choice: DC04+ZE | 1.0338

Send request!

1) Where no yield strength is defined, the respective values shall apply to the 0.2 % proof stress Rp0.2, otherwise for the lower yield strength (ReL). For thicknesses ≤ 0.7 mm, but > 0.5 mm, the maximum yield strength may be 20 MPa higher, and for thicknesses ≤ 0.5 mm 40 MPa.

2) For thicknesses ≤ 0.7 mm but > 0.5 mm, the minimum elongation at fracture may be 2 units lower. For thicknesses ≤ 0.5 mm, the minimum elongation at fracture may be 4 units lower.

3) The r90 and n90 values shown apply to product thicknesses ≥ 0.5 mm only.

4) For thicknesses > 2 mm, the r90 value is reduced by 0.2.