Choose your high strength IF steel here in grades HC180Y+ZE, HC220Y+ZE and HC260Y+ZE.
The experts at our locations are happy to advise you. We look forward to hearing from you.
Short name | VDA239-100* | Surface finish | Material number | Tensile strength R p0,2 1)MPa | Tensile strength RmMPa | Elongation at break A802)% min. | Anisotropy r903)4) | Solidification exponent n903) min. | Bake hardening index BH25) min. |
min. | |||||||||
HC180Y | CR180IF | +ZE | 1.0922 | 180-230 | 330-400 | 35 | 1.7 | 0.19 | - |
HC220Y | CR210IF | +ZE | 1.0925 | 220-270 | 340-420 | 33 | 1.6 | 0.18 | - |
HC260Y | CR240IF | +ZE | 1.0928 | 260-320 | 0 380-440 | 31 | 1.4 | 0.17 | - |
Short name | VDA239-100* | Material number | Mass fractions & max. | |||||||
---|---|---|---|---|---|---|---|---|---|---|
C | Si | Mn | P | S | AI min. | Ti6) | Nb6) | |||
HC180Y | CR180IF | 1.0922 | 0.01 | 0.3 | 0.7 | 0.06 | 0.025 | 0.01 | 0.12 | 0.09 |
HC220Y | CR210IF | 1.0925 | 0.01 | 0.3 | 0.9 | 0.08 | 0.025 | 0.01 | 0.12 | 0.09 |
HC260Y | CR240IF | 1.0928 | 0.01 | 0.3 | 1.6 | 01 | 0.025 | 0.01 | 0.12 | 0.09 |
1) If a pronounced yield point occurs, the values for the lower yield point (ReL) apply
2) For thicknesses ≤ 0.7 mm, but > 0.5 mm, minimum values for elongation at break that are 2 units lower are permissible. For thicknesses ≤ 0.5 mm, minimum values 4 units lower are permissible.
3) The minimum values for r90 and n90 only apply to product thicknesses ≥ 0.5 mm.
4) For product thicknesses > 2 mm, the r90 value is reduced by 0.2.
5) Special agreements must be made for thicknesses > 1.2 mm.
6) Vanadium and boron may also be added. The sum of the mass fractions of all four elements must not exceed 0.22%.
* Comparative grade, therefore slight deviations from DIN EN values possible
.