Choose your isotropic steel here in grades HC220I+ZE, HC260I+ZE and HC300I+ZE.
The experts at our locations are happy to advise you. We look forward to hearing from you.
Short name | VDA239-100* | Surface finish | Material number | Tensile strength R p0,2 1)MPa | Tensile strength RmMPa | Elongation at break A802)% min. | Anisotropy r903)4) | Solidification exponent n903) min. | Bake hardening index BH25) min. |
min. | |||||||||
HC220I | - | +ZE | 1.0346 | 220-270 | 300-380 | 34 | 1.4 | 0.18 | - |
HC260I | - | +ZE | 1.0349 | 260-310 | 320-400 | 32 | 1.4 | 0.17 | - |
HC300I | - | +ZE | 1.0447 | 300-350 | 340-440 | 30 | 1.4 | 0.16 | - |
Short name | VDA239-100* | Material number | Mass fractions & max. | |||||||
---|---|---|---|---|---|---|---|---|---|---|
C | Si | Mn | P | S | AI min. | Ti6) | Nb6) | |||
HC220I | – | 1.0346 | 0.07 | 0.5 | 0.6 | 0.05 | 0.025 | 0.015 | 0.05 | – |
HC260I | – | 1.0349 | 0.07 | 0.5 | 1.2 | 0.05 | 0.025 | 0.015 | 0.05 | – |
HC300I | – | 1.0447 | 0.08 | 0.5 | 0.7 | 0,08 | 0.025 | 0.015 | 0.05 | – |
1) If a pronounced yield point occurs, the values for the lower yield point (ReL) apply
2) For thicknesses ≤ 0.7 mm, but > 0.5 mm, minimum values for elongation at break that are 2 units lower are permissible. For thicknesses ≤ 0.5 mm, minimum values 4 units lower are permissible.
3) The minimum values for r90 and n90 only apply to product thicknesses ≥ 0.5 mm.
4) For product thicknesses > 2 mm, the r90 value is reduced by 0.2.
5) Special agreements must be made for thicknesses > 1.2 mm.
6) Vanadium and boron may also be added. The sum of the mass fractions of all four elements must not exceed 0.22%.
* Comparative grade, therefore slight deviations from DIN EN values possible
.