Choose your electrolytically zinc-coated Retained-austenite steel (TRIP steel) here in grades HCT690T+ZE and HCT780T+ZE.
The experts at our locations are happy to advise you. We look forward to hearing from you.
Short name | VDA239-100* | Surface finish | Material number | Tensile strength R p0,2 MPa | Tensile strength RmMPa | Elongation at break A802)% min. | Solidification exponent nn10-UEmin. | Bake hardening index BH25) min. |
HCT690T | CR400Y690T-TR | +ZE | 1.0947 | 400-520 | 690 | 23 | 0.19 | 40 |
HCT780T | CR450Y780T-TR | +ZE | 1.0948 | 450-570 | 780 | 21 | 0.16 | 40 |
1) XG = dual phase with increased yield strength
2) Reduced minimum values of elongation at break apply to product thicknesses t < 0.60 mm (minus 2 units). * Comparative grade, therefore slight deviations from DIN EN values possible
3) Elongation at break for a proportional sample with L0 = 5.65 √S0 for sheet thicknesses ≥ 3.0 mm
Short name | VDA239-100* | Surface finish | Material number | Mass % max. | ||||||||||
---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|
C | Si | Mn | P | S | AItotal(from/to) | Cr+Mo | Nb+Ti | V | B | |||||
HCT690T | CR400Y690T-TR | +ZE | 1.0947 | 0.24 | 2.00 | 2.20 | 0.080 | 0.015 | 0.015-2.0 | 0,60 | 0.20 | 0.20 | 0.005 | |
HCT780T | CR450Y780T-TR | +ZE | 1.0948 | 0.25 | 2.20 | 2.50 | 0.080 | 0.015 | 0.015-2.0 | 0.60 | 0.20 | 0.20 | 0.005 |
1) XG = dual phase with increased yield strength
* Comparative grade, therefore slight deviations from DIN EN values possible
.