DX56D | 1.0963

Grade DX56D is a special deep drawing grade and is suitable for the highest forming requirements.

Low-carbon steel for cold forming

Properties according to DIN EN 10 346

Steel type

Short designation	VDA239-100*	Surface finish	Material number
DX56D	CR4	+Z,+ZA	1.0963
DX56D	CR4	+ZF,+ZM	1.0963
DX56D	CR4	+AZ,+AS	1.0963

* Comparative grade, therefore minor deviations from DIN EN values possible

DX56D | 1.0963: Mechanical properties (transverse)

Yield strength ¹⁾ Re MPa max.	Tensile strength Rm MPa	Elongation at ²⁾ fracture A80 % min.	Anisotropy r90 min.	Strain hardening exponent n90 min.
120–180	260–350	39	1.9⁴⁾	0.21
120–180	260–350	37	1.7⁴⁾⁵⁾	0.20⁵⁾
120–180	260–350	39	1.7⁴⁾⁵⁾	0.20⁵⁾

DX56D | 1.0963: Chemical composition (heat analysis)

Percentage by weight % max.
C	Si	Mn	P	S	Ti
0.12	0.50	0.60	0.10	0.045	0.30

Your product of choice: DX56D | 1.0963

Send request!

1) Where no yield strength is defined, the respective values shall apply to the 0.2 % proof stress Rp0.2, otherwise for the lower yield strength (ReL).

2) Reduced minimum values of elongation at fracture apply to product thicknesses 0.50 mm < t < 0.70 mm (minus 2 units), 0.35 mm < t < 0.50 mm (minus 4 units), and t < 0.35 mm (minus 7 units).

3) The maximum yield strength for surface class A is Re = 360 MPa.

4) For product thicknesses of 1.5 mm < t < 2 mm, the minimum r90 value is reduced by 0.2, and for t ≥ 2 mm by 0.4.

5) Depending on the product thickness, the minimum r90 value is reduced as follows: 0.50 mm < t < 0.70 mm by 0.2; 0.35 mm < t < 0.50 mm by 0.4, and t < 0.35 mm by 0.6.

Also depending on the product thickness, the minimum n90 value is reduced as follows: 0.50 mm < t < 0.70 mm by 0.01; 0.35 mm < t < 0.50 mm by 0.03, and t < 0.35 mm by 0.04.