HX300LAD | 1.0932

Grade HX300LAD belongs to the micro-alloyed steels and has a yield strength of at least 300 MPa.

Micro-alloyed steel

HX300LAD | 1.0932: Properties according to DIN EN 10 346

Steel type

Short designation	VDA239-100*	Surface finish	Material number
HX300LAD	CR270LA	+Z,+ZF,+ZA,+ZM,+AZ,+AS	1.0932

* Comparative grade, therefore minor deviations from DIN EN values possible

HX300LAD | 1.0932: Mechanical properties (transverse)

Proof stress Rp 0,2 ¹⁾MPa	Tensile strength Rm MPa	Elongation at fracture ²⁾³⁾ % A80
300–380	380–480	23

HX300LAD | 1.0932: Chemical composition (heat analysis)

Percentage by weight % max.
C	Si	Mn	P	S	Al min.	Nb	Ti
0.12	0.50	1.4	0.030	0.025	0.015	0.09	0.15

Your product of choice: HX300LAD | 1.0932

Send request!

1) Where the yield yield strength is defined, the respective values shall apply to the the lower yield strength (ReL).

2) Depending on the product thickness, the minimum values of elongation at fracture are reduced as follows: 0.50 mm < t < 0.70 mm (minus 2 units), 0.35 mm < t < 0.50 mm (minus 4 units), and t < 0.35 mm (minus 7 units).

3) For AS, AZ, ZF and ZM coatings, the minimum A80 value is reduced by 2 units and the minimum r90 value by 0.2.

4) For product thicknesses of 1.5 mm < t < 2 mm, the minimum r90 value is reduced by 0.2, and for t ≥ 2 mm by 0.4.

5) Depending on the product thickness, the minimum r90 value is reduced as follows: 0.50 mm < t < 0.70 mm by 0.2; 0.35 mm < t < 0.50 mm by 0.4, and t < 0.35 mm by 0.6. Also depending on the product thickness, the minimum n90 value is reduced as follows: 0.50 mm < t < 0.70 mm by 0.01; 0.35 mm < t < 0.50 mm by 0.03, and t < 0.35 mm by 0.04.