S315MC | 1.0972
Thanks to its fine-grained microstructure and high degree of purity, grade S315MC is well suited for cold bending, folding and cold flanging without cracking. The name of grade S315MC refers to its upper yield strength. This is 315 MPa.
The following minimum values for the bending radii should be considered:
Thermomechanically rolled steel for cold working
Nominal thickness (t), mm | Min. bending radius |
<= 3 | 0.25 t |
3< t <=6 | 0.5 t |
t >6 | 1.0 t |
S315MC | 1.0972: Properties according to DIN EN 10 149-2
Steel type
Short designation | VDA239-100 | Material number |
S315MC | HR300LA | 1.0972 |
S315MC | 1.0972: Mechanical properties, longitudinal
Upper yield1) strength ReH MPa min. | Tensile strength Rm MPa | Elongation at fracture A80 % min. | Elongation at fracture A5 % min. |
315 | 390–510 | 20 | 24 |
S315MC | 1.0972: Chemical composition (heat analysis)
Percentage by weight % max. | ||||||||
C | Mn | Si | P | S | Altotal min. | Nb | V | Ti |
0.12 | 1.30 | 0.50 | 0.025 | 0.020 | 0.015 | 0.092) | 0.202) | 0.15 2) |
Your product of choice: S315MC | 1.0972
1) For thicknesses > 8 mm the yield strength values may be 20 MPa lower.
2) The combined content of Nb, V and Ti must not exceed 0.22 %.