S550MC | 1.0986

Thanks to its fine-grained microstructure and high degree of purity, grade S550MC is well suited for cold bending, folding and cold flanging without cracking. The name of grade S550MC refers to its upper yield strength. This is 550 MPa.

S550MC - send request!

The following minimum values for the bending radii should be considered:

Thermomechanically rolled steel for cold working

Nominal thickness (t), mm	Min. bending radius
<= 3	1.0 t
3< t <=6	1.5 t
t >6	2.0 t

S550MC | 1.0986: Properties according to DIN EN 10 149-2

Steel type

Short designation	VDA239-100	Material number
S550MC	HR550LA	1.0986

S550MC | 1.0986: Mechanical properties, longitudinal

Upper yield¹⁾ strength ReH MPa min.	Tensile strength Rm MPa	Elongation at fracture A80 % min.	Elongation at fracture A80 % min.
550	600–760	12	14

S550MC | 1.0986: Chemical composition (heat analysis)

Percentage by weight % max.
C	Mn	Si	P	S	Altotal min.	Nb	V	Ti
0.12	1.80	0.50	0.025	0.015	0.015	0.09²⁾	0.20²⁾	0.15 ²⁾

Your product of choice: S550MC | 1.0986

Send request!

1) For thicknesses > 8 mm the yield strength values may be 20 MPa lower.

2) The combined content of Nb, V and Ti must not exceed 0.22 %.

Also available with closer thickness tolerances in the form of scalur® (see page 19) or from the Basque Mungia as in accordance with DIN EN 10 140.