S600MC | 1.8969

Thanks to its fine-grained microstructure and high degree of purity, grade S600MC is well suited for cold bending, folding and cold flanging without cracking. The name of grade S600MC refers to its upper yield strength. This is 600 MPa.

S600MC - send request!

The following minimum values for the bending radii should be considered:

Thermomechanically rolled steel for cold working

Nominal thickness (t), mm	Min. bending radius
<= 3	1.0 t
3< t <=6	1.5 t
t >6	2.0 t

S600MC | 1.8969: Properties according to DIN EN 10 149-2

Steel type

Short designation	VDA239-100*	Material number
S600MC	-	1.8969

* Comparative grade, therefore minor deviations from DIN EN values possible

S600MC | 1.8969: Mechanical properties, longitudinal

Upper yield¹⁾strength ReH MPa min.	Tensile strength Rm MPa	Elongation at fracture A80 % min.	Elongation at fracture A³⁾ % min.
600	650–820	11	13

S600MC | 1.8969: Chemical composition (heat analysis)

Percentage by weight % max.
C	Mn	Si	P	S	Altotal min.	Nb	V	Ti	Mo	B
0.12	1.90	0.50	0.025	0.015	0.015	0.09²⁾	0.20²⁾	0.15 ²⁾	0,50	0,005

Your product of choice: S600MC | 1.8969

Send request!

1) For thicknesses > 8 mm the yield strength values may be 20 MPa lower.

2) The combined content of Nb, V and Ti must not exceed 0.22 %.

3) Percentage elongation after fracture using a proportional specimen with L₀ = 5.65 √S₀ for sheet thicknesses ≥ 3.0 mm.

Available with a narrower range of mechanical properties and increased elongation at fracture.