DC06 | 1.0873

Grade DC06 exhibits excellent deep-drawing properties under all types of deformation. This special deep drawing grade is suitable for the highest forming requirements and is one of the high-quality, low-carbon Ti alloy IF steels. DC06 is therefore particularly suitable for difficult deep-drawn and stretch-formed parts such as sidewalls, oil pans and bottom plates.

DC06 - send request!

Mild low-carbon steel for cold forming

DC06 | 1.0873: Properties according to DIN EN 10 130

Steel type

Short designation	VDA239-100*	Material number
DC06	CR5	1.0873

* Comparative grade, therefore minor deviations from DIN EN values possible

DC06 | 1.0873: Mechanical properties (transverse)

Yield strength¹⁾ Re MPa max.	Tensile strength Rm MPa	Elongation at fracture²⁾% min. A80	Anisotropy r90³⁾⁴⁾min.	Strain hardening exponent n90³⁾min.
170	270-330	41	2.1	0.220

DC06 | 1.0873: Chemical composition (heat analysis)

Percentage by weight % max.
C	P	S	Mn	Ti
0.02	0.020	0.020	0.25	0.3

Your product of choice: DC06 | 1.0873

Send request!

1) Where no yield strength is defined, the respective values shall apply to the 0.2 % proof stress (Rp0.2) or to the lower yield strength (ReL). For thicknesses ≤ 0.7 mm but > 0.5 mm, the maximum yield strength values may be 20 MPa higher. In case of thicknesses ≤ 0.5 mm, the maximum yield limits may be 40 MPa higher.

2) For thicknesses ≤ 0.7 mm but > 0.5 mm, the minimum elongation at fracture may be 2 units lower. For thicknesses ≤ 0.5 mm, the minimum elongation at fracture may be 4 units lower.

3) The r90 and n90 values apply to product thicknesses ≥ 0.5 mm only.

4) For thicknesses > 2 mm, the r90-value is reduced by 0.2.