cold-rolled sheet

DC07 | 1.0898

Grade DC07 exhibits excellent deep-drawing capability under all types of deformation. This super deep drawing grade is suitable for extreme forming requirements and is one of the high-quality, low-carbon Ti alloy IF steels. DC07 is therefore particularly suitable for difficult deep-drawing and stretch-forming parts such as side walls, oil pans and bottom plates.

Mild low-carbon steel for cold forming

Properties according to DIN EN 10 130

Steel type

Short designationVDA239-100Material number
DC07-1.0898

Mechanical properties (transverse)

Yield strength1) Re MPa max.Tensile strength Rm MPaElongation at fracture2) % min. A80Anisotropy r903)4) min.Strain hardening exponent n903) min.
150250-310442.50.230

Chemical composition (heat analysis)

Percentage by weight % max.
CPSMnTi
0.10.0200.0200.200.2

1) Where no yield strength is defined, the respective values shall apply to the 0.2 % proof stress (Rp0.2) or to the lower yield strength (ReL). For thicknesses ≤ 0.7 mm but > 0.5 mm, the maximum yield strength values may be 20 MPa higher. In case of thicknesses ≤ 0.5 mm, the maximum yield limits may be 40 MPa higher.

2) For thicknesses ≤ 0.7 mm but > 0.5 mm, the minimum elongation at fracture may be 2 units lower. For thicknesses ≤ 0.5 mm, the minimum elongation at fracture may be 4 units lower.

3) The r90 and n90 values apply to product thicknesses ≥ 0.5 mm only.

4) For thicknesses > 2 mm, the r90-value is reduced by 0.2.