HC420LA | 1.0556

Grade HC420LA belongs to the cold-rolled microalloyed steels and has a 0.2% yield strength of around 420 MPa.

Micro-alloyed steel

Properties according to DIN EN 10 268

Steel type

Short designation	VDA239-100*	Material number
HC420LA	CR380LA	1.0556

* Comparative grade, therefore minor deviations from DIN EN values possible

HC420LA | 1.0556: Mechanical properties (transverse)

Proof stress Rp 0.2¹⁾MPa	Tensile strength Rm MPa	Elongation at fracture A²⁾ % 80 min.
420–520	470–600	17

HC420LA | 1.0556: Chemical composition (heat analysis)

Percentage by weight % max.
C	Si	Mn	P	S	Al min.	Ti⁶⁾	Nb ⁶⁾
0.14	0.5	1.6	0.03	0.025	0.015	0.15	0.09

Your product of choice: HC420LA | 1.0556

Send request!

1) Where no yield strength is defined, the respective values shall apply to the lower yield strength (ReL)

2) For thicknesses ≤ 0.7 mm but > 0.5 mm, the minimum elongation at fracture may be 2 units lower. For thicknesses ≤ 0.5 mm, the minimum elongation at fracture may be 4 units lower.

3) The r90 and n90 minimum values apply to product thicknesses ≥ 0.5 mm only.

4) For thicknesses > 2 mm, the r90 value is reduced by 0.2.

5) For thicknesses > 1.2 mm, special arrangements are required.

6) Additions of vanadium and boron are also permissible. The total content of all four elements must not exceed 0.22 % .