HC300LA+ZE | 1.0489

Grade HC300LA+ZE belongs to the electrolytically zinc-coated sheets and has a 0.2% yield strength of around 300 MPa.

Properties according to DIN EN 10 268

Steel type

Short designation	VDA239-100	Surface finish	Material number
HC300LA	CR270LA	+ZE	1.0489

Micro-alloyed steel

HC300LA+ZE | 1.0489: Mechanical properties (transverse)

Proof stress Rp 0,2¹⁾ MPa	Tensile strength Rm MPa	Elongation at²⁾ fracture A80 % min.
300–380	380–480	23

HC300LA+ZE | 1.0489: Chemical composition (heat analysis)

Percentage by weight % max.
C	Si	Mn	P	S	AI	Ti⁶⁾	Nb⁶⁾
0.12	0.5	1.4	0.03	0.025	0.015	0.15	0.09

Your product of choice: HC300LA+ZE | 1.0489

Send request!

1) Where a yield strength is defined, the respective values shall apply to the lower yield strength (ReL)

2) For thicknesses ≤ 0.7 mm but > 0.5 mm, the minimum elongation at fracture may be 2 units lower. For thicknesses ≤ 0.5 mm, the minimum elongation at fracture may be 4 units lower.

6) Additions of vanadium and boron are also permissible. The total content of all four elements must not exceed 0.22 % .

* Comparative quality, therefore slight deviations from DIN EN values possible